The application of hot-dipped zinc and zinc-aluminum alloy (35%, 55%, 82% Al) coatings were introduced. Exposure tests of the steels with these coatings were conducted in the offshore atmosphere in Qingdao and Xiamen for 12 years separately. Effects of the coating thickness, alloy composition and atmospheric environment on the corrosion performance were studied. Results of the onsite exposure tests were compared with the results of a previous indoor salt spray accelerated corrosion tests. The study supports that zinc-aluminum alloy coatings are useful in providing better corrosion resistance and can be further developed for future applications.
Corrosion resistance of hot-dipped zinc and zinc alloy coated sheet steels under offshore atmospheric environment
Korrosionsbeständigkeit von Feuer-Zink und -Zinklegierungsüberzügen auf Stahlblechen in der Atmosphäre einer Offshore-Anlage
Materials and Corrosion ; 58 , 8 ; 616-620
2007
5 Seiten, 6 Tabellen, 4 Quellen
Aufsatz (Zeitschrift)
Englisch
Korrosionsbeständigkeit , verzinkter Stahl , metallischer Überzug , Feuerverzinken , Zink , Zinkaluminiumlegierung , Aluminiumzinklegierung , Feldversuch , Off-Shore-Anlage , atmosphärische Korrosion , Meeresatmosphäre , China , Aggressivität , Bewitterungsversuch , Salzsprühprüfung , Korrosionsgeschwindigkeit
Selection of Zinc and Zinc-Alloy (Hot-Dipped and Electrodeposited) Coated Steel Sheet
SAE Technical Papers | 1999
Selection of Zinc and Zinc-Alloy (Hot-Dipped and Electrodeposited) Coated Steel Sheet
SAE Technical Papers | 2009
Selection of Zinc and Zinc-Alloy (Hot-Dipped and Electrodeposited) Coated Steel Sheet
SAE Technical Papers | 2015
Corrosion Behavior of Painted Zinc and Zinc Alloy Coated Autobody Sheet Steels
SAE Technical Papers | 1986
|Corrosion testing and behaviour of zinc and zinc alloy coated autobody sheet steels
Tema Archiv | 1988
|