YP460 MPa class heavy thick plate with excellent crack arrestability for mega container carriers has been developed. Advanced alloy design and optimized controlled rolling and cooling process using Super-OLAC (On-Line Accelerated Cooling) are applied to obtain highly oriented textures parallel to the surface of the plate, which are effective to prevent brittle crack propagation. Crack arrest toughness (Kca at -10 °C) of the developed steel is 16800 N/mm3/2, which is more than double of the guidelines on brittle crack arrest design issued by Class NK. The large scale duplex ESSO test, assuming the structure of hatch side coaming of container carriers, was also carried out, and the result revealed that the developed steel plate has excellent performance to stop brittle crack propagation. The developed steel plate is supposed to be utilized to ensure the safety of mega container carriers against the brittle fracture.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Development of YP460 N/mm2 class heavy thick plate with excellent brittle crack arrestability for mega container carriers


    Weitere Titelangaben:

    Entwicklung schwerer Grobbleche mit einer Mindeststreckgrenze von 460 MPa mit ausgezeichnetem Sprödrissauffangvermögen für große Containerschiffe
    Titel japanisch


    Beteiligte:
    Hase, Kazukuni (Autor:in) / Hansa, Tsunehisa (Autor:in) / Eto, Taiki (Autor:in)

    Erschienen in:

    JFE Giho ; 33 ; 13-18


    Erscheinungsdatum :

    2014


    Format / Umfang :

    6 Seiten, 8 Bilder, 7 Tabellen, 19 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Japanisch




    Development of YP460 class steel plate with excellent brittle crack arrestability for large container ships

    Murakami, Yoshiaki / Takeuchi, Yoshiko / Hase, Kazukuni et al. | Tema Archiv | 2013


    WELDED STRUCTURE HAVING EXCELLENT BRITTLE CRACK ARRESTABILITY

    Europäisches Patentamt | 2021

    Freier Zugriff

    WELDED STRUCTURE HAVING EXCELLENT BRITTLE CRACK ARREST CHARACTERISTICS

    HANDA TSUNEHISA / IGI SATOSHI / OI KENJI et al. | Europäisches Patentamt | 2017

    Freier Zugriff

    WELDED STRUCTURE HAVING EXCELLENT BRITTLE CRACK ARREST CHARACTERISTICS

    HANDA TSUNEHISA / IGI SATOSHI / OI KENJI et al. | Europäisches Patentamt | 2017

    Freier Zugriff

    The effect of shear-lips on the arrestability of thicker steel plates

    Funatsu, Yuuji / Shirahata, Hiroyuki / Otani, Jun et al. | Tema Archiv | 2012