A three steps 3D cohesive element based modelling procedure for hydrogen embrittlement susceptibility prediction of an X70 weld thermal simulated Heat Affected Zone has been developed. Fracture mechanics testing both under electrochemical charging and pressurized hydrogen gas are used for simulations validation. A new approach for the cohesive parameter's choice, based on the initial cohesive stiffness entity, has been adopted. The best fit to the experimental data were obtained for cohesive strength of 14,450 MPa and for opening of 0.005 mm, yielding a reduced threshold stress intensity KIC,HE of 49 MPa√m, for test in CP. Hydrogen boundary condition for simulations of test under hydrogen gas obtained by applying Sievert's law provided far too low concentrations for any appreciable influence on the cohesive energy. Toward the end of the paper, comparison between the two hydrogen sources is made by imposing the same initial hydrogen boundary conditions for the simulations. Results indicate that crack initiation is located at the hydrostatic stress peak and at the crack tip for cathodic protection and 0.6 MPa H2 gas conditions, respectively. Simulations suggest that the hydrogen in lattice interstitials is mainly responsible for the embrittlement.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    3D cohesive modelling of hydrogen embrittlement in the heat affected zone of an X70 pipeline steel – Part II


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2014


    Format / Umfang :

    14 Seiten, 30 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    3D cohesive modelling of hydrogen embrittlement in the heat affected zone of an X70 pipeline steel

    Alvaro, Antonio / Olden, Vigdis / Akselsen, Odd Magne | Tema Archiv | 2013


    Study on local embrittlement of welding heat-affected zone in X80 pipeline steels

    Shiying, Hao / Gao, Huilin / Zhang, Xiaoyong et al. | Tema Archiv | 2011


    Hydrogen embrittlement of high strength pipeline steels

    Hardie, D. / Charles, E.A. / Lopez, A.H. | Tema Archiv | 2006