The relationship between the microstructure and toughness of welding heat-affected zone in Z80 grade pipeline steels is studied. It is found that the intercritical reheated coarse-grained heat-affected zone (ICCGHAZ) of experimental steels has the lowest toughness values when the secondary peak temperature is at intercritical (α +γ) region during multi-pass welding. The local embrittlement is mainly attributed to the morphology, amount and size of M-A constituent. It is also found that the microstructural inhabitance at ICCGHAZ has a deleterious effect on the toughness. On the basis of above experimental results, it is suggested that the local embrittlement should be prevented by using pre-heating thermal cycle which could eliminate the microstructural inhabitance and using post-heating thermal cycle which could improve the morphology, amount and size of M-A constituent.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study on local embrittlement of welding heat-affected zone in X80 pipeline steels


    Beteiligte:
    Shiying, Hao (Autor:in) / Gao, Huilin (Autor:in) / Zhang, Xiaoyong (Autor:in) / Yong, Zhou (Autor:in)

    Erschienen in:

    China Welding ; 20 , 2 ; 36-40


    Erscheinungsdatum :

    2011


    Format / Umfang :

    5 Seiten, 8 Bilder, 2 Tabellen, 5 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch