The investigated seamless pipe line steel grade X80 achieved good/excellent impact energies over a wide range of welding parameters. Hardness values below 300 HV10 can be attained within a wide parameter range as well. It has been shown that it is generally possible to achieve low HAZ hardness values (below 250 HV10) in the reheated CG HAZ which is the most critical area. To verify the sour gas resistance of the produced weld seams SSC tests will be performed. In practice it seems to be more reasonable to apply post weld heat treatment if hardness values below 250 HV10 are required for all areas of the weld seam. The heat treatment parameters have to be accurately chosen to get softening of the martensitic structures and avoid hardening by precipitations.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Weldabilty of heavy wall seamless line pipe steel X80


    Beteiligte:
    Wiebe, Joerg (Autor:in) / Bruns, Claas (Autor:in) / Toma, Diana (Autor:in)


    Erscheinungsdatum :

    2013


    Format / Umfang :

    7 Seiten, 13 Bilder, 6 Tabellen, 8 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch




    Conveying frame for seamless steel pipe machining

    SHEN YANG | Europäisches Patentamt | 2024

    Freier Zugriff

    SEAMLESS STEEL PIPE AND INFLATOR BOTTLE FOR AIRBAGS

    AOKI KOSUKE / NAKAMURA HIROFUMI | Europäisches Patentamt | 2024

    Freier Zugriff

    Development of High Strength and Heavy Wall Line Pipe

    Takeuchi, I. / Nagase, M. / Sakaguchi, I. et al. | British Library Conference Proceedings | 1993


    Seamless steel tube for heavy hoisting machinery

    YUAN CHUNHUI | Europäisches Patentamt | 2020

    Freier Zugriff

    Steel pipe auxiliary supporting tool for maintenance of seamless steel pipe of air conditioner

    HUANG JINGSONG / LING FENG / YU QINGCHUN et al. | Europäisches Patentamt | 2024

    Freier Zugriff