In this study, electrochemical impedance spectroscopy (EIS) technique was used to investigate the development of stress corrosion cracking (SCC) in X70 pipeline steels. Slow strain rate testing (SSRT) was performed on steel samples in high pH bicarbonate solution. Calculation of impedance data for cracks during slow strain rate testing. Potentiostatic EIS tests were also conducted regularly to determine the changes associated with the SCC. The Bode modulus and phase diagrams for cracks were calculated. Furthermore, the suitable frequency window for detection of the cracks by EIS was determined. Proposing a circuit model for stress corrosion cracking of X70 pipeline steel. Trend of phase angle shift and impedance modulus for X70 steel during SSRT. Finally, a circuit model proposed for the cracking.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Electrochemical impedance spectroscopy analysis of X70 pipeline steel stress corrosion cracking in high pH carbonate solution


    Weitere Titelangaben:

    Elektrochemische impedanzspektroskopische Analyse der Spannungsrisskorrosion des Rohrstahles X70 in Carbonatlösungen mit hohem pH-Wert


    Beteiligte:
    Oskuie, A.A. (Autor:in) / Shahrabi, T. (Autor:in) / Shahriari, A. (Autor:in) / Saebnoori, E. (Autor:in)

    Erschienen in:

    Corrosion Science ; 61 ; 111-122


    Erscheinungsdatum :

    2012


    Format / Umfang :

    12 Seiten, 17 Bilder, 2 Tabellen, 28 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch