According to the study of the microstructure and properties of X100 pipeline steel, the welding consumable-wire based on Mn-Ni-Mo-B-Ti alloy system was successfully designed and developed. The yield strength of the deposited metal of the developed welding wire was 695 MPa, the tensile strength was 810 MPa, and Charpy impact energy was 92 J at -20 °C when matching with BSG-SJ101H1 sintered flux. The results of the weldability test for X100 pipeline steel which adopting this developed wire showed that the tensile strength of the weld was 827 MPa, 185 J of Charpy impact energy (-10 °C) , 97% of section of shear and the weld had good strength and toughness matching when the welding speed got to 1.7 m/min. The microstructure and fracture appearance of the weld were analyzed by using metallographic microscope, scanning electron microscope (SEM) and laser confocal microscope, the results indicated that the microstructure ivas mainly granular bainite in the weld metal, and the fracture was dimple with 200 - 300 µm depth presenting a typical ductile fracture characteristics. The test of welding wire with different content of Ni and Cr element indicated that Ni was better than Cr in improving the strength and toughness of weld metal.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Research on submerged arc welding wire for XI00 pipeline steel


    Beteiligte:
    Zongyue, Bi (Autor:in) / Liu, Haizhang (Autor:in) / Xiaotian, Jing (Autor:in) / Hui, Niu (Autor:in)

    Erschienen in:

    China Welding ; 20 , 2 ; 56-62


    Erscheinungsdatum :

    2011


    Format / Umfang :

    7 Seiten, 4 Bilder, 3 Tabellen, 10 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Weldability and SAW welding wire of X80 pipeline steel

    Huang, Zhijun / Hu, Lunji / Kai, Miao et al. | Tema Archiv | 2006




    Submerged Arc Welding SAW . Submerged Arc Welding only Transfer-type welding equipment.

    AN DONG SOO / HYUN JONG HO | Europäisches Patentamt | 2018

    Freier Zugriff