The effect of Cr content on resistance to CO2-induced corrosion was investigated for low alloyed pipeline steels by using high-pressure high-temperature autoclave with electrochemical measurement, while the morphologies of corrosion product scales were observed by scanning electron microscope (SEM). The results showed that Cr-enrichod compact corrosion product scales might form on the steels with addition of a little amount of Cr in CO2 containing environments, in other words, the resistance to C02-corrosion of the steels could be enhanced significantly by the addition of Cr. With the increasing of Cr content the average corrosion rate and the resistance to local corrosion of the steels were improved markedly. The corrosion potential of pipeline steels shifted to more positive values, and the polarization resistance increased with the increasing Cr content, which agreed with the analysis result of average corrosion rate.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Cr content on resistance to CO2-induced corrosion of low alloy pipeline steels


    Weitere Titelangaben:

    Titel chinesisch


    Beteiligte:
    Hu, Li-hua (Autor:in) / Yu, Man-li (Autor:in) / Chang, Wei (Autor:in) / Zhang, Lei (Autor:in) / Xu, Li-ning (Autor:in) / Lu, Min-xu (Autor:in)


    Erscheinungsdatum :

    2011


    Format / Umfang :

    5 Seiten, 7 Bilder, 2 Tabellen, 10 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Unbekannt




    DROPLET CORROSION ON CO2 TRANSPORT PIPELINE STEELS

    Hoa, L. / Kratzig, A. / Babler, R. et al. | TIBKAT | 2018


    Effect of loading history on hydrogen content in pipeline steels

    Vadhwana, N.M. / Chen, W. | Tema Archiv | 2002


    Corrosion Resistance of Trip Steels

    A. J. Baghdasarian | NTIS | 1972


    Mechanistic investigation of deflected stress corrosion cracking in pipeline steels

    Xie, Jeffrey / Yang, Lin / Sen, Millan et al. | Tema Archiv | 2009


    Effect of Mn and MnS on corrosion properties of domestic pipeline steels and welds

    Li, Yuntao / Du, Zeyu / Tao, Yongyin et al. | Tema Archiv | 2004