Setting conditions for the avoidance of in-service crack growth in aggressive corroding environments has long been a major challenge owing to the number of variables that have a significant effect on material behaviour. The fatigue behaviour of API 5L X65 pipeline steel parent material tested in a sour environment has been investigated. Fatigue crack growth rate (FCGR) tests have been performed to evaluate the influence of crack depth on crack growth rate (da/dN), over the range 2-10 mm. The results obtained showed crack growth rates for deep flaws to be a factor of 5-30 higher in the sour environment than in air, dependent on the applied stress intensity factor range (Delta K). Shallow flaws have been shown to grow up to an order of magnitude faster than deep flaws in a sour environment at the same value of Delta K. The results highlight a potential non-conservatism associated with using deep-crack data to predict the behaviour of shallow flaws. The observed behaviour is attributed to the uptake of hydrogen at specimen surfaces exposed to the sour environment.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of crack depth on fatigue crack growth rates for a C-Mn pipeline steel in a sour environment


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2010


    Format / Umfang :

    9 Seiten, 25 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    An investigation into fatigue crack growth test methods in a sour environment

    Holtam, Colum M. / Baxter, David P. / Ashcroft, Ian A. et al. | Tema Archiv | 2009


    Crack growth in microalloyed pipeline steels for sour gas transport

    Serna, S. / Campillo, B. / Albarran, J.L. | Tema Archiv | 2005


    Assessment of pipeline fatigue crack-growth life

    Jaske, Carl E. | Tema Archiv | 2007



    Near-threshold fatigue crack growth behavior and crack closure of natural gas pipeline steels

    Kim, Young-Pyo / Kim, Cheol-man / Kim, Woo-sik et al. | Tema Archiv | 2011