A fundamentally based mathematical model was developed with the goal to predict, as a first step, the crack growth rate (CGR) of high pH stress corrosion cracking (SCC) of buried steel pipelines. Two methods were used to predict CGRs and for both methods the model has included the film rupture and repassivation mechanism. The two methods are distinguished by the expression used to determine the active anodic current density at the crack tip. In the first method, this current density is expressed by the anodic polarization curve with a large peak current density and the prediction tends to yield a larger CGR and a lower pH at the crack tip. By contrast, when the Butler-Volmer equation is used to express the crack tip anodic current density, with a predicted low CGR the chemistry at the tip does not appear to have any significant change due to the high buffer of the solution. The predicted mechanism responsible for the steady-state crack growth is shown to be the balance between the increasing stress intensity factor as the crack grows, which tends to increase the crack tip strain rate and thus the CGR, and the change of the crack tip condition, which, for large CGRs, is the significant shift in the more negative direction of the crack tip potential, and for low CGRs, the increase of ferrous ion concentration, and either tends to decrease CGR.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Predicting the mechanisms and crack growth rates of pipelines undergoing stress corrosion cracking at high pH


    Weitere Titelangaben:

    Vorhersage von Mechanismus und Risswachstumsgeschwindigkeit von Rohrleitungen bei Spannungsrisskorrosion bei hohem pH-Wert


    Beteiligte:
    Song, F.M. (Autor:in)

    Erschienen in:

    Corrosion Science ; 51 , 11 ; 2657-2674


    Erscheinungsdatum :

    2009


    Format / Umfang :

    18 Seiten, 35 Bilder, 2 Tabellen, 65 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch