An engineering approach has been developed for assessing the fitness-for-service (FFS) of pipelines that operate in environments where they are subject to stress-corrosion cracking (SCC). This approach employs J-integral fracture mechanics to quantify the growth of SCC flaws and assess the potential for fracture-toughness failure. An effective flaw area model is used to assess the potential for flow-strength failure. This paper reviews the development of the FFS approach, describes recent improvements to it, and discusses its validation by comparison with the results of laboratory testing and field experience. Procedures for estimating fracture toughness and predicting pipeline fracture are presented. Available data on SCC growth rates are reviewed, and their use in the prediction of remaining safe operating life is discussed. Two examples are presented to illustrate the application of the FFS approach.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fitness-for-service assessment for pipelines subject to stress-corrosion cracking


    Beteiligte:
    Jaske, C.E. (Autor:in) / Beavers, J. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2000


    Format / Umfang :

    10 Seiten, 30 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Failure criteria for stress-corrosion cracking in pipelines

    Leis, B. N. / Mohan, R. / Delanty, B. S. et al. | British Library Conference Proceedings | 1995


    Modeling Stress-Corrosion Cracking of High-Pressure Gas Pipelines

    Leis, B. N. / Parkins, R. N. / American Gas Association; Pipeline Research Committee | British Library Conference Proceedings | 1993


    Residual stress and stress corrosion cracking of high pressure hydrocarbon transmission pipelines

    Van Boven, Greg / Rogge, Ronald / Chen, Weixing | Tema Archiv | 2007


    Internal stress-corrosion cracking in anthropogenic CO2 pipelines: is it possible?

    Sandana, D. / Dale, M. / Charles, E.A. et al. | British Library Online Contents | 2013