It has been observed in the shipping industry that the rate of corrosion of steel plate may increase with longer duration of exposure, typically over many years. This effect has been attributed to the flexure of ships plates causing the loss of protective rust layers. The present paper describes the results of laboratory experiments in which plates with pre-existing rusts were subject to high levels of tensile strain, with and without subsequent exposure and corrosion. All rusts were obtained by exposing the steel to a natural marine environment, including the atmospheric and tidal zones. Careful observation of the rusts under tensile strain conditions showed that only strains near and beyond the elastic limit of the steel have the capacity to cause significant damage to the rust layers. Subsequent short-term exposure tests on pre-corroded and pre-strained steel coupons showed that there can be a moderate (10-15%) increase in the short-term corrosion rate.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of tensile strain on the rate of marine corrosion of steel plates


    Weitere Titelangaben:

    Einfluss von Zugbelastung auf die Korrosionsgeschwindigkeit von Stahlplatten in Meeresatmosphäre


    Beteiligte:

    Erschienen in:

    Corrosion Science ; 51 , 10 ; 2298-2303


    Erscheinungsdatum :

    2009


    Format / Umfang :

    6 Seiten, 8 Bilder, 3 Tabellen, 18 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Tensile strength behaviour of steel plates with corrosion-induced geometrical deteriorations

    Vukelic, Goran / Vizentin, Goran / Ivosevic, Spiro | Taylor & Francis Verlag | 2022



    Effect of Strain Rate on Tensile Properties of Textiles

    Husain, I. / Pal, S. K. / Thakare, V. B. et al. | British Library Conference Proceedings | 1999


    Effects of high strain rate on tensile properties of 10Ni5CrMoV hull steel

    Li, Hui / Gao, Ling-qing / Sun, Jian-ke | Tema Archiv | 2007