The effect of strain rate on room temperature tensile properties of 10Ni5CrMoV hull steel was investigated at die strain rates between 1.6x10-3 - 1.2x103 per s. The experimental results show that strain rate doesn't affect the fracture mechanism of intragranular dimple and mainly dislocation slipping; the tensile strength is increased slightly along with the increase of strain rate, however, the elongation doesn't decrease in general which is decreased firstly and raised later with the increase of strain rate, the high strain rate doesn't embrittle the 10Ni5CrMoV steel. The experimental results can be explained by dislocation slipping.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of high strain rate on tensile properties of 10Ni5CrMoV hull steel


    Weitere Titelangaben:

    Einfluss einer hohen Dehnrate auf die mechanischen Eigenschaften des Schiffbaustahls 10Ni5CrMoV
    Titel chinesisch


    Beteiligte:
    Li, Hui (Autor:in) / Gao, Ling-qing (Autor:in) / Sun, Jian-ke (Autor:in)

    Erschienen in:

    Iron and Steel, Peking ; 42 , 12 ; 77-80


    Erscheinungsdatum :

    2007


    Format / Umfang :

    4 Seiten, 5 Bilder, 1 Tabelle, 8 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Unbekannt






    High strain rate tensile properties of a woven glass fabric composite

    Greenfield, Robert / Vinson, Jack / Telegadas, Harry | AIAA | 1997


    High Strain Rate Tensile Properties of a Woven Glass Fabric Composite

    Greenfield, R. / Vinson, J. / Telegadas, H. et al. | British Library Conference Proceedings | 1996


    High strain rate tensile properties of a woven glass fabric composite

    Greenfield, Robert / Vinson, Jack / Telegadas, Harry | AIAA | 1998