The phenomenon of Abnormal Grain Growth (AGG) was studied in a Fe-1%Si alloy using automated Electron Backscattered Dfffraction (EBSD). Industrially processed samples that were temper rolled to 0%, 1.5% and 8% were annealed in air for various times followed by quenching in water. The results obtained were compared to those from heat treatments performed in wet 15%H2-85%N2 at a US Steel facility. In addition, for a more complete study, the 1.5% temper-rolled material was heat-treated in other atmospheres such as 5%H2-95%Ar, 98%H2-2%He, 98%H2-2%H2S, and 98%H2-2%N2 for 1 hour followed by quenching in water. AGG was observed in every annealing atmosphere considered, but occurred most rapidly in samples annealed in air. In general, grains of varying orientations grew abnormally resulting in uniform coverage of the Standard Stereographic Triangle (SST). One consistently observed trend was that the matrix grains either did not coarsen or only coarsened very slowly; the Abnormally Large Grains (ALG), were, on average, approximately 10 times the size of the matrix. The grain boundary character of the interfaces between abnormal grains and the matrix was analyzed. There was no significant variation from the overall population of boundaries;general high angle boundaries were mainly observed and special boundary types did not appear with particularly high (or low) frequencies. This suggested that the grain boundary character of these materials does not control AGG. The role of stored energy differences was evaluated by examining the orientation gradients in each grain. Grains that grew abnormally had low orientation gradients. This suggests that stored energy differences are present even in the 0% temper rolled material and that variations in stored energy were the main driving force for the AGG observed in this Fe-1%Si alloy.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Abnormal grain growth in Fe-1percent Si driven by stored energy differences


    Weitere Titelangaben:

    Anormales Kornwachstum im Fe-1%Si-Stahl getrieben durch Unterschiede bei gespeicherter Energie


    Beteiligte:
    Bennett, T. (Autor:in) / Kalu, P.N. (Autor:in) / Rollett, A.D. (Autor:in)


    Erscheinungsdatum :

    2006


    Format / Umfang :

    9 Seiten, 8 Bilder, 20 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Abnormal Grain Growth in S-816 Alloy

    Rush, A I / Freeman, J W / White, A E | NTRS | 1952


    Abnormal Grain Growth in Nickel-base Heat-resistant Alloys

    Decker, R F / Rush, A I / Dano, A G et al. | NTRS | 1957


    Stored pressure driven cycle

    MINICK ALAN B / KOKAN TIMOTHY S / LITTLES JERROL W | Europäisches Patentamt | 2019

    Freier Zugriff

    Electric Stored Energy Source

    MERTENS THOMAS | Europäisches Patentamt | 2020

    Freier Zugriff

    Stored energy transmission system

    Baker, A. | Tema Archiv | 1976