In modern technology, analysis of fatigue behaviour of engineering components is obligatory to develop engines and mechanical parts to improve the performance and to increase lifetime up to 109 cycles. On the other hand, the estimations and analysis of the mechanism of fatigue failure must be known in detail for steel industry to develop high quality steels. In this research, different alloys, failed under high frequency fatigue conditions, used in the automotive industry, were studied: steels, heat treated at different conditions, cast iron and cast aluminium with different tensile strength ranging from 220 to 2350 MPa. These alloys were tested at very high cycle-gigacycle-fatigue (VHCF, >107), using a piezoelectric fatigue system (20 kHz) under tension-compression conditions with a stress ratio of R = -1. The central part of each specimen was cooled by compressed air to keep the temperature constant at room temperature. Fatigue failure values were usually located between 107 and 1010 cycles. Effects of defect types on failure mechanism in very high cycle fatigue range are discussed here in detail with fracture surface analysis by using Scanning Electron Microscopy (SEM).


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failure mechanisms of automotive metallic alloys in very high cycle fatigue range


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2006


    Format / Umfang :

    13 Seiten, 17 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    FATIGUE CRACKING MECHANISMS OF TITANIUM ALLOY VT3-1 IN VERY-HIGH-CYCLE-FATIGUE REGIME

    A. A. Shanyavskiy / C. Bathia / A. D. Nikitin et al. | DOAJ | 2016

    Freier Zugriff

    Very High Cycle Fatigue of Cast Aluminum Alloys under Variable Humidity Levels

    Engler-Pinto, Carlos / Cui, Haitao / Wen, Weidong et al. | SAE Technical Papers | 2015


    Very High Cycle Fatigue of Cast Aluminum Alloys under Variable Humidity Levels

    Li, Wenkai / Cui, Haitao / Wen, Weidong et al. | British Library Conference Proceedings | 2015


    Ermüdungsverhalten faserverstärkter Kunststoffe im Very High Cycle Fatigue-Bereich

    Adam, Till Julian / Technische Universität Braunschweig | GWLB - Gottfried Wilhelm Leibniz Bibliothek | 2016


    Very High Cycle Fatigue Behavior of TA11 Titanium Alloy

    JIAO Zehui / YU Huichen / ZHONG Bin et al. | DOAJ | 2017

    Freier Zugriff