The conventional fatigue test method was used to obtain the very high cycle fatigue (VHCF) limits of 3×107 and 1×108 cycles for TA11 titanium alloy in different temperatures and stress ratios. Three parameter power function method was used to obtain the VHCF median S-N curves and equations. The results show that the VHCF strength of 3×107 and 1×108 cycles presented a continue reducing trend compared with the traditional 1 x 107 fatigue limit. This trend is not obvious in negative stress ratio (R=-1), but significant in normal stress ratio (R=0.1 and 0.5), and the reduction amplitude of room temperature tests was greater than that of elevated temperature tests. The fracture morphologies showed that the VHCF cracks initiat at the specimen surface of TA11 alloy in room temperature tests, and the VHCF cracks initiation ways in elevated temperature tests relate to the stress ratio. The cracks initiate at the specimen surface when R=0.1 and 0.5 but in the internal when R=0.5; The surface state of TA11 alloy specimens is the main cause of its fatigue life dispersion.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Very High Cycle Fatigue Behavior of TA11 Titanium Alloy


    Beteiligte:
    JIAO Zehui (Autor:in) / YU Huichen (Autor:in) / ZHONG Bin (Autor:in) / LI Xudong (Autor:in) / ZHOU Jingyi (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    FATIGUE CRACKING MECHANISMS OF TITANIUM ALLOY VT3-1 IN VERY-HIGH-CYCLE-FATIGUE REGIME

    A. A. Shanyavskiy / C. Bathia / A. D. Nikitin et al. | DOAJ | 2016

    Freier Zugriff

    Fracture behavior of low cycle fatigue and dwell fatigue of Ti6242 titanium alloy under high load

    ZHANG Mingda / CAO Jingxia / SUI Nan et al. | DOAJ | 2019

    Freier Zugriff

    Effect of Humidity on the Very High Cycle Fatigue Behavior of a Cast Aluminum Alloy

    Engler-Pinto, Carlos / Cui, Haitao / Wen, Weidong et al. | SAE Technical Papers | 2016


    Fatigue crack propagation behavior of high strength titanium alloy

    WANG Huan / XIN Shewei / GUO Ping et al. | DOAJ | 2024

    Freier Zugriff