In this paper, fatigue tests on a cast aluminum alloy (AS7GU-T64) were performed under different frequencies and humidity levels. Tests conducted under conventional frequency in laboratory air have been compared to tests conducted under ultrasonic frequency in dry air, saturated humidity and in distilled water. It was observed that the highest and lowest fatigue lives correspond to ultrasonic fatigue tests in dry air and in distilled water, respectively. Unlike specimens tested at conventional frequency, all of the specimens tested at ultrasonic frequency presented a large amount of slip facets on the fatigue crack propagation fracture surface.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Humidity on the Very High Cycle Fatigue Behavior of a Cast Aluminum Alloy


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:
    Engler-Pinto, Carlos (Autor:in) / Cui, Haitao (Autor:in) / Wen, Weidong (Autor:in) / Li, Wenkai (Autor:in) / Su, Xuming (Autor:in)

    Kongress:

    SAE 2016 World Congress and Exhibition ; 2016



    Erscheinungsdatum :

    05.04.2016


    Format / Umfang :

    7 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Effect of Humidity on the Very High Cycle Fatigue Behavior of a Cast Aluminum Alloy

    Li, Wenkai / Engler-Pinto, Carlos / Cui, Haitao et al. | British Library Conference Proceedings | 2016


    Very High Cycle Fatigue of Cast Aluminum Alloys under Variable Humidity Levels

    Engler-Pinto, Carlos / Cui, Haitao / Wen, Weidong et al. | SAE Technical Papers | 2015


    Very High Cycle Fatigue of Cast Aluminum Alloys under Variable Humidity Levels

    Li, Wenkai / Cui, Haitao / Wen, Weidong et al. | British Library Conference Proceedings | 2015


    Effect of humidity on the very high cycle fatique behavior of a cast aluminium alloy

    Li,W. / Engler-Pinto,C. / Cui,H. et al. | Kraftfahrwesen | 2016


    Low cycle fatigue of A356-T6 cast aluminum alloy

    Wigant,C.C. / Stephens,R.I. / Univ.of Iowa,US | Kraftfahrwesen | 1987