The results of 12 years of outdoor corrosion testing of steel sheet coated with 5 % AL-Zn plus Mischmetal are presented. It was observed that in severe marine environment, coating thickness losses are initially greater for conventional galvanized sheet that for steel sheet coated with 5 % Al-Zn plus MM. It was also observed that conventional galvanized sheet is more durable than steel sheet coated with 5 % Al-Zn plus MM. The results show that there is no significance differences in corrosion rates of a conventional galvanized coating and a 5 % Al-Zn + MM coatings.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Atmospheric corrosion resistance of steel sheet coated with 5% Al-Zn plus mischmetal


    Weitere Titelangaben:

    Atmosphärische Korrosionsbeständigkeit von mit 5 %Al-Zn plus Mischmetall beschichteten Stahlblechen


    Beteiligte:

    Erschienen in:

    Materials Performance ; 44 , 11 ; 28-31


    Erscheinungsdatum :

    2005


    Format / Umfang :

    4 Seiten, 8 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Undervehicle corrosion resistance of 55 % Al-Zn coated steel sheet

    Allegra, L. / Townsend, H.E. | Tema Archiv | 1981


    Corrosion resistance of aluminium coated stainless steel sheet under marine environment

    Hatanaka, N. / Hattori, Y. / Miyoshi, Y. et al. | Tema Archiv | 1989


    Corrosion Behavior of Organic Composite Coated Steel Sheet

    Mochizuki, Kazuo / Yamato, Koji / Morito, Nobuyuki et al. | SAE Technical Papers | 1993


    Corrosion behavior of organic composite coated steel sheet

    Sujita,S. / Muko,R. / Mochizuki,K. et al. | Kraftfahrwesen | 1993