Reliability analysis of tank car structures undergoing fatigue crack growth and general corrosion (tank wall thinning) is illustrated to support informed decision-making and planning for reliability-centered maintenance. Two specific mechanisms that contribute to tank car deterioration are considered: (1) corrosion with negligible fatigue crack growth; and (2) corrosion-accelerated fatigue crack growth. Reliability analysis of corrosion-accelerated fatigue crack growth is performed with a time-dependent tank wall thickness reduction and a fatigue crack growth model that incorporates a three-degrees-of-freedom surface crack obeying Walker crack growth law under tank car spectrum loading. System reliability problems involving multiple corrosion sites are considered to illustrate important features of failure probability for a series system in relation to failure probability of individual corrosion sites.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Structural reliability analysis of railroad tank cars subjected to fatigue and corrosion


    Beteiligte:
    Zhao, Wei (Autor:in) / Sutton, Michael A. (Autor:in)


    Erscheinungsdatum :

    2005


    Format / Umfang :

    13 Seiten, 25 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    A methodology for assessing fatigue crack growth reliability of railroad tank cars

    Zhao, Wei / Sutton, Michael A. / Pena, Jose | Tema Archiv | 2004


    Damage Tolerance Analysis of Railroad Tank Cars

    Zhao, W. / Sutton, M. A. / Pena, J. et al. | British Library Conference Proceedings | 2000


    Fire protection for railroad tank cars

    Johnson, M.R. | Tema Archiv | 1986


    Materials used in railroad tank cars

    Graves, C.T. | Engineering Index Backfile | 1959


    Painting setup for railroad tank cars

    Krohne, J. | Engineering Index Backfile | 1964