A methodology for assessing structural reliability of railroad tank cars undergoing fatigue crack growth is being developed. A three-degree-of freedom (3-dof) surface crack is employed to account for an asymmetric stress field existing at a fatigue critical location in tank car structures. A fatigue life prediction program using the Walker equation to account for stress ratio effects is developed for the 3-dof surface crack model. A component reliability problem is formulated as a limit state function and solved using a first-order reliability method along with importance sampling method within the commercial reliability software, STRUREL. The methodology is demonstrated using illustrative railroad tank car examples. The results show that: (a) failure probability, Pt, increases as tank car mileage increases; (b) welding residual stresses in the tank structure can significantly increase Pf; (c) uncertainty in the stress amplitude also has a significant effect on Pf; and (d) the correlation between initial crack depth and initial crack aspect ratio is an important parameter.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A methodology for assessing fatigue crack growth reliability of railroad tank cars


    Beteiligte:
    Zhao, Wei (Autor:in) / Sutton, Michael A. (Autor:in) / Pena, Jose (Autor:in)


    Erscheinungsdatum :

    2004


    Format / Umfang :

    15 Seiten, 27 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch






    Assessing Derailment Potential of Partially Filled Railroad Tank Cars

    Hunter, Mark / Marquis, Brian / Greif, Robert et al. | British Library Conference Proceedings | 2020


    Fire protection for railroad tank cars

    Johnson, M.R. | Tema Archiv | 1986


    JRC2020-8038 Assessing Derailment Potential of Partially Filled Railroad Tank Cars

    Hunter, Mark / Marquis, Brian / Greif, Robert et al. | TIBKAT | 2020