For upgrading long-term integrity of transmission pipelines, two types of delayed fracture in regions of mechanical damage in pipelines were investigated. Experimental and numerical studies clarified factors affecting the fatigue behavoir of line pipes containing an idealized flaw under fluctuating internal pressure. To investigate fatigue cracking at mechanical damage in pipelines, degradation of fracture toughness and fatigue properties dur to plastic prestrain was also evaluated. A fracture mechanics-based study revealed conditions necessarily for initiation of HSC (hydrogen stress cracking) at a surface defect in line pipes under cathodic protection.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Factors affecting long-term integrity of transmission pipelines


    Weitere Titelangaben:

    Faktoren, die die Langzeit-Integrität von Pipelines beeinflussen


    Beteiligte:
    Hagiwara, N. (Autor:in) / Masuda, T. (Autor:in) / Oguchi, N. (Autor:in)


    Erscheinungsdatum :

    2000


    Format / Umfang :

    12 Seiten, 6 Bilder, 15 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch





    Pipeline integrity of ethylene pipelines

    Nordquist, Greg | Tema Archiv | 2005


    Condition based integrity assessment of pipelines

    Kumar, Amrita / Hannum, Robert / Beard, Shawn J. et al. | Tema Archiv | 2007


    Seismic integrity of high-strength pipelines

    Suzuki, Nobuhisa / Igi, Satoshi / Masamura, Katsumi | Tema Archiv | 2007