Cathodic disbonding, blistering, and current demand for cathodic protection were measured for nine commercial coatings for submerged steel structures. The ASTM-G8 standard test and a long-term test (2 years), simulating North Sea conditions, were used. The relevance of the ASTM-G8 test as a prequalification test was evaluated by comparing cathodic disbonding in the two tests. After 800 days in the long-term test, the correlation to ASTM-G8 was good. The correlation coefficient was 0.98. The current demand for cathodic protection increased when the coating blistered. Examination of the blisters showed that they had cracked. After 2 years of testing, the current demand only had increased for the coatings (<150 micrometers). The current demand for the thicker coatings (>450 micrometers) had not increased, in spite of significant cathodic disbonding for some coatings. Coating breakdown factors, defined as the ratio between current demand for cathodic protection for the coated samples and samples of bare steel, were calculated. These factors were compared with the design values for cathodic protection in Det Norske Veritas (DNV) RP B401 and NORSOK M-CR-503. For all coatings, the coating breakdown rate was lower than the design values.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of cathodic disbonding and blistering on current demand for cathodic protection of coated steel


    Weitere Titelangaben:

    Einfluß der kathodischen Enthaftung und der Blasenbildung auf den Strombedarf für den kathodischen Schutz von beschichtetem Stahl


    Beteiligte:
    Knudsen, O.O. (Autor:in) / Steinsmo, U. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 56 , 3 ; 256-264


    Erscheinungsdatum :

    2000


    Format / Umfang :

    9 Seiten, 10 Bilder, 3 Tabellen, 30 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Factors influencing the rate of cathodic disbonding of coatings

    Steinsmo, U. / Skar, J.I. | Tema Archiv | 1994


    Effects of hydrotalcite intercalated with corrosion inhibitor on cathodic disbonding of epoxy coatings

    Hang, T. T. / Duong, N. T. / Truc, T. A. et al. | British Library Online Contents | 2015


    System for impressed current cathodic protection

    VAN DELDEN MARC | Europäisches Patentamt | 2023

    Freier Zugriff

    SYSTEM FOR IMPRESSED CURRENT CATHODIC PROTECTION

    VAN DELDEN MARC | Europäisches Patentamt | 2021

    Freier Zugriff

    Monitoring cathodic protection

    Moran, D. | Tema Archiv | 1984