Glass core and hollow core chalocogenide fibers were fabricated and coated with Teflon cladding for protection. The dimensions of the hollow core fiber were 30-600μm OD, 20-500μm ID and up to tens of meters in length. Attenuation measurements were performed with a lead salt tunable diode laser as well as with a CO2 laser. The power loss due to bending for a fiber with a hollow core, and the far field power distribution of this kind of fiber, are also reported. Spectral dependence of the fibers in the region 10-13 μm was obtained using diode lasers. The advantages of glass core and hollow core fibers are discussed.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Hollow And Glass Core Chalcogenide Fibers


    Beteiligte:
    Bornstein, A. (Autor:in) / Boehm, L. (Autor:in)

    Kongress:

    Infrared Optical Materials and Fibers IV ; 1986 ; Los Angeles,CA,United States


    Erschienen in:

    Erscheinungsdatum :

    1986-05-12





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Chalcogenide Infrared Glass Fibers

    Bornstein, A. / Croitoru, N. / Marom, E. | SPIE | 1982



    Research In KRS-5 And Chalcogenide Glass Fibers

    Devyatykh, G. G. / Dianov, E. M. | SPIE | 1984


    Low-loss infrared arsenic-chalcogenide glass optical fibers

    Devyatykh, Grigory G. / Dianov, Eugeni M. / Plotnichenko, Victor G. et al. | SPIE | 2000


    Heterophase impurity inclusions in chalcogenide glass optical fibers

    Devyatykh, Grigory G. / Churbanov, Mikhail F. / Scripachev, I. V. et al. | SPIE | 1990