This paper reports recent achievements in the field of infrared optical fibers based on vitreous arsenic chalcogenides (As2S3, As2Se3, As2Se1.5Te1.5). The minimum optical losses of the fibers from arsenic sulfide, arsenic selenide and arsenic telluride are equal to 20 - 30 dB/km at 2.2 and 3.3 micrometers , 80 - 100 dB/km at 4.3 micrometers , and 100 - 300 dB/km and 6.7 micrometers , respectively. Among them the double polymer coated two-layer arsenic-sulfide optical fibers have the lowest optical losses (20 - 25 dB/km) and the highest mechanical bending strength (1 - 1.5 GPa).


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Low-loss infrared arsenic-chalcogenide glass optical fibers


    Beteiligte:

    Kongress:

    Advances in Fiber Optics ; 2000 ; Moscow,Russian Federation


    Erschienen in:

    Erscheinungsdatum :

    2000-05-17





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Chalcogenide Infrared Glass Fibers

    Bornstein, A. / Croitoru, N. / Marom, E. | SPIE | 1982


    Development and Infrared Applications of Chalcogenide Glass Optical Fibers

    Sanghera, J. S. / Shaw, L. B. / Busse, L. E. et al. | British Library Online Contents | 2000



    Chalcogenide Glass Fibers for Infrared Sensing and Space Optics

    Bureau, B. / Maurugeon, S. / Charpentier, F. et al. | British Library Online Contents | 2009


    Heterophase impurity inclusions in chalcogenide glass optical fibers

    Devyatykh, Grigory G. / Churbanov, Mikhail F. / Scripachev, I. V. et al. | SPIE | 1990