A comprehensive scanning electron microscope(SEM) survey of the fracture surfaces of an aircraft main landing gear shock strut piston showed that improper shot peening contributed to the initiation of the anamolous fatigue failure.SEM photographs of the suspect-origin regions and the surrounding areas were analyzed. The photographs are presented, along with a detailed description of the regions observed. Failure mechanism is discussed, and causes of fracture origin explored.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failure Analysis of a Shot-Peened Component


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Johari, Om (Autor:in) / Sipes, William A. (Autor:in)

    Kongress:

    National Automobile Engineering Meeting ; 1973



    Erscheinungsdatum :

    01.02.1973




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Shot-peened gear failure due to operation in a misaligned condition

    COUCHON, D. / BARNES, G. / CEDOZ, R. | AIAA | 1993





    Geometric Structure of the Surface of Impulse Shot-Peened Titanium Alloy Ti6Al4V

    Skoczylas, Agnieszka / Matuszak, Jakub / Ciecielag, Krzysztof et al. | IEEE | 2024