An extensive field study was made of the corrosion of aluminum alloy panels in over fifteen years of service in three regions of the USA. Panels removed from service exposed vehicles were subjected to further testing to determine the relationship between field service, accelerated laboratory corrosion testing, and marine environment exposure for two years at Daytona Beach, Florida.In addition, two 42 year old aluminum bodied Dyna Panhard vehicles were recovered in France, examined closely, and subjected to similar tests.Few examples of significant corrosion were found in the field, and only one example of filiform corrosion on aluminum sheet in service. Steel panels on the same vehicles frequently rusted through, and filiform corrosion was seen occasionally. Laboratory tested aluminum panel samples frequently showed filiform corrosion and severe intergranular corrosion. No filiform corrosion on recovered panels has been observed to date at the Daytona Beach site, although some laboratory prepared samples exhibit general corrosion. Performance of aluminum alloy panels is clearly superior to steel.Many laboratory corrosion tests in current use are far too severe, and do not predict actual service behavior. The relevance of accelerated testing to service behavior is discussed.
The Corrosion Performance of Aluminum Automotive Body Panels in Service
Sae Technical Papers
International Congress & Exposition ; 1998
1998-02-23
Aufsatz (Konferenz)
Englisch
Aluminum alloys , Aluminum , Body panels , Steel , Corrosion
Corrosion performance of aluminum automotive body panels in service
Tema Archiv | 1998
|The corrosion performance of aluminum automotive body panels in service
Kraftfahrwesen | 1998
|Aluminum for automotive body sheet panels
TIBKAT | 1998
Forming of Automotive Aluminum Body Panels by Sheet Hydroforming
Tema Archiv | 2013
|Corrosion-resistant precoated steel shets for automotive body panels
Tema Archiv | 1988
|