Unexpected severe failures occur during the warm forming procedure of carbon fiber material due to the existence of extremely large deformation/strain. To evaluate this failure, a good understanding the accurate material property under certain loading is important to evaluate the forming feasibility of carbon fiber material. Also, a clear connection between the fiber orientation and the material property helps to increase the accuracy of the forming prediction. Therefore, an experimental test is needed to evaluate the material property as well as the fiber orientation. In this paper, a uniaxial tension test for the prepreg carbon fiber under the warm forming condition is performed. A halogen lamp is used to heat the specimen to reach the warm forming condition. A 3D Digital Image Correlation (3D-DIC) is utilized to measure the material property and the fiber orientation in this test, along with a DIP system. The strain distribution, dimension change, and the fiber orientation are measured throughout the test. The detailed experimental procedure is demonstrated, and the result is also analyzed.
Property and Fiber Orientation Determination for Carbon Fiber Composite
Sae Technical Papers
WCX World Congress Experience ; 2018
03.04.2018
Aufsatz (Konferenz)
Englisch
Property and Fiber Orientation Determination for Carbon Fiber Composite
British Library Conference Proceedings | 2018
|Controlled-Orientation Short-Fiber Composite Bodies
Online Contents | 1998
Carbon fiber composite laminate generation method, carbon fiber composite laminate and automobile
Europäisches Patentamt | 2024
|Effects of Fiber and Property Orientation on “C” Shaped Cross Sections
SAE Technical Papers | 1991
|Effects of fiber and property orientation on "C" shaped cross section
Kraftfahrwesen | 1991
|