This study aims to determine some mechanical properties of an Inconel 718 aged superalloy obtained through hot tensile tests. These properties as conventional 0.2% yield strength (σv), ultimate strength (σUTS), and specific elongation assessment (εu) are important parameters in the study of the mechanical material behavior. The superalloy was subjected to hot tensile tests at 650 to 700°C and a strain rate of 0.5 mm/min according to ASTM E-8. It is used a scanning electron microscope (SEM) to obtain images of the fracture surface of the specimens. The images of the fracture surface are analyzed in order to relate the temperature of the test with the type of mechanism of fracture.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study of the Mechanical Behavior of an Inconel 718 Aged Superalloy Submitted to Hot Tensile Tests


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    SAE Brasil 2011 Congress and Exhibit ; 2011



    Erscheinungsdatum :

    04.10.2011




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Study of the Mechanical Behavior of an Inconel 718 Aged Superalloy Submitted to Hot Tensile Tests

    Caliari, F.R. / Candioto, K.C.G. / Reis, D.A.P. et al. | British Library Conference Proceedings | 2011


    CREEP ANALYSIS OF INCONEL 718 AGED SUPERALLOY AT 675^oC

    Caliari, F.R. / Reis, D.A.P. / De Moura Neto, C. et al. | British Library Conference Proceedings | 2012


    Creep Analysis of Inconel 718 Aged Superalloy at 675°C

    Couto, Antonio A. / de Moura Neto, Carlos / Nunes, Carlos A. et al. | SAE Technical Papers | 2012


    Study of the Fractography of Inconel 718 Superalloy After Creep Mechanical Test

    Sugahara, T. / Reis, D.A.P. / de Moura Neto, C. et al. | British Library Conference Proceedings | 2011


    Study of the Fractography of Inconel 718 Superalloy After Creep Mechanical Test

    de Moura Neto, Carlos / Reis, Danieli A. P. / Piorino Neto, Francisco et al. | SAE Technical Papers | 2011