This work intends to analyze the influence of the stress and temperatures used in creep mechanical tests in the types of fractures that occurred in the superalloy Inconel 718. For this, the superalloy was subjected to creep tests under the conditions 625 to 814 MPa at temperatures of 650, 675 and 700°C. After the tests, the fractured samples were cleaned on an ultrasound and subjected to microstructural analysis using the technique of scanning electron microscopy. Images were performed with different increases in order to analyze the type of fracture that occurred in the material. The elongated sample and its reduction in area were also measured in order to study the effects of different conditions used in the creep tests under material's fracture.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study of the Fractography of Inconel 718 Superalloy After Creep Mechanical Test


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE Brasil 2011 Congress and Exhibit ; 2011



    Erscheinungsdatum :

    2011-10-04




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Creep Analysis of Inconel 718 Aged Superalloy at 675°C

    Couto, Antonio A. / de Moura Neto, Carlos / Nunes, Carlos A. et al. | SAE Technical Papers | 2012


    Tensile Strain Hardening Behavior and Fractography of Superalloy GH39

    WANG Hui / CHENG Minghe / ZHANG Chengxiang et al. | DOAJ | 2016

    Freier Zugriff


    Study of the Mechanical Behavior of an Inconel 718 Aged Superalloy Submitted to Hot Tensile Tests

    Couto, Antonio A. / de Moura Neto, Carlos / Nunes, Carlos A. et al. | SAE Technical Papers | 2011