The strength and failure mode of a resistance spot weld between two sheets of steel are shown to be dependent upon the thickness and yield strength of the base material, the diameter of the weld, the strength of the weld metal, and the restraint imposed by the material surrounding the weld. A relationship is developed which makes possible the reliable calculation of the weld diameter required to cause heat affected zone failure around the weld when loaded in shear. It applies to plain carbon steel and the high strength, micro-alloyed steels of up to 690 Mpa (100,000 psi) yield strength. This relationship along with another relating weld failure load to the base metal strength form the basis for a proposed weldability criteria for low carbon steel.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Ultimate Strength and Failure Mode of Spot Welds in High Strength Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1977 International Automotive Engineering Congress and Exposition ; 1977



    Erscheinungsdatum :

    1977-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Ultimate Load Capacity of Spot Welds Made of Ultra High Strength Steels

    Blaski, Brad / Chen, Chris / Zywicki, Gregory et al. | SAE Technical Papers | 2011


    Ultimate Load Capacity of Spot Welds Made of Ultra High Strength Steels

    Zhang, Z. / Chen, C. / Zywicki, G. et al. | British Library Conference Proceedings | 2011


    Fatigue strength of spot welds in titanium-bearing HSLA-steels

    Pollard,B. / Jones and Laughlin Steel,Pittsburgh,US | Kraftfahrwesen | 1982