Failure mode and fatigue behavior of friction stir spot welds made with convex and concave tools in lap-shear specimens of dissimilar high strength dual phase steel (DP780GA) and hot stamped boron steel (HSBS) sheets are investigated based on experiments and a kinked fatigue crack growth model. Lap-shear specimens with the welds were tested under both quasistatic and cyclic loading conditions. Optical micrographs indicate that under both quasi-static and cyclic loading conditions, the welds mainly fail from cracks growing through the upper DP780GA sheets where the tools were plunged in during the welding processes. Based on the observed failure mode, a kinked fatigue crack growth model is adopted to estimate fatigue lives of the welds. In the kinked crack fatigue crack growth model, the stress intensity factor solutions for fatigue life estimations are based on the closed-form solutions for idealized spot welds in lap-shear specimens. The fatigue life estimations are reasonably in agreement with the experimental results under low-cycle loading conditions but lower than the experimental results under high-cycle loading conditions.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failure Mode and Fatigue Behavior of Friction Stir Spot Welds in Lap-Shear Specimens of Dissimilar Advanced High Strength Steels


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:
    Pan, Jwo (Autor:in) / Avery, Katherine (Autor:in) / Santella, Michael (Autor:in) / Hong, Seung Hoon (Autor:in) / Pan, Tsung-Yu (Autor:in) / Feng, Zhili (Autor:in)

    Kongress:

    SAE 2013 World Congress & Exhibition ; 2013



    Erscheinungsdatum :

    08.04.2013


    Format / Umfang :

    7 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Failure Mode and Fatigue Behavior of Friction Stir Spot Welds in Lap-Shear Specimens of Dissimilar Advanced High Strength Steels

    Hong, S.H. / Avery, K. / Pan, J. et al. | British Library Conference Proceedings | 2013




    Fatigue Behavior of Dissimilar 5754/7075 and 7075/5754 Spot Friction Welds in Lap-Shear Specimens

    Pan, Jwo / Pan, Tsung-Yu / Tran, Van-Xuan | SAE Technical Papers | 2010


    Fatigue Behavior of Dissimilar Ultrasonic Spot Welds in Lap-Shear Specimens of Magnesium and Steel Sheets

    Franklin, T.J. / Pan, J. / Santella, M. et al. | British Library Conference Proceedings | 2011