The use of chromium and manganese as alloying additions to water atomized steels is possible; provided, the manganese and chromium oxides that are formed during the powder production are reduced prior to forging the sintered preform. One way of reducing the chromium and manganese oxides is through the use of high temperature sintering; that is, sintering at temperatures in excess of 1204°C. Utilizing a sintering temperature of either 1260°C or 1315°C, lowers the residual oxygen contents of the 4100 and 1500 type powders to approximately 500 ppm and 400 ppm, respectively. At these low levels of residual oxygen content, the Charpy impact toughness of the chromium-manganese and manganese alloy steels is comparable to the Charpy toughness of the commercially available nickel-molybdenum alloy powder steels. One advantage to the use of high temperature sintering is the ability to shorten the sintering cycle from 30 minutes normally utilized at 1120°C to 5 to 10 minutes at either 1260°C or 1315°C. This shortened sintering time can result in reduced sintering cost. The reduced sintering cost coupled with the lower cost of the chromium and manganese alloying elements result in a significant cost savings when compared to the nickel-molybdenum powder steels.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Mechanical Properties of Powder Forged 4100 and 1500 Type Alloy Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1981



    Erscheinungsdatum :

    1981-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Mechanical properties of powder forged 4100 and 1500 type alloy steels

    Neiderman,J.M. / Hoeganaes,Riverton,US | Kraftfahrwesen | 1981


    High Strength 4100 Alloy P/M Steels

    Rodrigues, Heron / Sanderow, Howard I. | SAE Technical Papers | 1986


    Nr. 4100

    DataCite | 1924


    Material characterisation of powder-forged copper steels

    Chernenkoff,R.A. / Hall,D.W. / Mocarski,S. et al. | Kraftfahrwesen | 1991


    Material Characterization of Powder-Forged Copper Steels

    Hall, D.W. / Gagné, M. / Chernenkoff, R.A. et al. | SAE Technical Papers | 1991