The sintered and heat treated properties of 4100 prealloyed powder (0.9Cr, 0.8 Mn, 0.25Mo) were examined over a range of densities (6.8, 7.1, and 7.2 gm/cm3 and carbon contents (0.25, 0.5, and 0.9%). The effect of alloying elements on as-sintered UTS was also studied. For comparison, elementally blended 4600 was used as a “standard” wherever practical.In the “as-sintered” condition, 4100 offers exceptionally superior mechanical properties especially at higher carbons, which exceed even the heat treated properties of conventionally processed 4600 alloy, In the heat treated condition, there are no significant differences between the two alloys, but the superior hardenability of 4100 makes it more attractive.Potential automotive applications are identified where 4100 can be a candidate to replace heat treated P/M forged or wrought components.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High Strength 4100 Alloy P/M Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1986



    Erscheinungsdatum :

    1986-03-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Mechanical Properties of Powder Forged 4100 and 1500 Type Alloy Steels

    Neiderman, Joel M. | SAE Technical Papers | 1981


    Mechanical properties of powder forged 4100 and 1500 type alloy steels

    Neiderman,J.M. / Hoeganaes,Riverton,US | Kraftfahrwesen | 1981


    Nr. 4100

    DataCite | 1924


    HIGH STRENGTH LOW ALLOY STEELS

    Parker, Charles M. | SAE Technical Papers | 1954


    High strength alloy P/M steels

    Sanderow,H.I. / Rodrigues,H. / Stanadyne,Supermet Div.,US | Kraftfahrwesen | 1986