This study compares the hot corrosion resistance of several internal combustion engine exhaust valve alloys in a simulated diesel engine environment. Hot corrosion of exhaust valves occurs when deposits accumulate on the head and are subjected to temperatures between 650 to 1000°C. Test specimens were subjected to a mixture of CaSO4, BaSO4, Na2SO4, and carbon at 870°C. The materials tested included head material specimens and valves with cobalt based or nickel based seat facings. The depth of corrosion penetration was measured and the valve base materials and seat face coatings were ranked accordingly. The results indicate that nickel based valve alloys have poorer sulfidation resistance than iron based alloys, and nickel based seat facings accelerate the corrosive attack on the base material in the faced region as compared to the unfaced portion of the valve. Valves with cobalt base Tribaloy seat facings exhibited the best resistance, followed by the iron base, Stellite and nickel base respectively.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Hot Corrosion Studies of Automotive Exhaust Valves


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Larson, Jay M. (Autor:in) / Ari-Gur, Pnina (Autor:in) / Narasimhan, Simon (Autor:in) / Noble, Victoria (Autor:in)

    Kongress:

    International Congress & Exposition ; 1991



    Erscheinungsdatum :

    1991-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Hot corrosion studies of automotive exhaust valves

    Pnina,A. / Noble,V. / Narasimhan,S. et al. | Kraftfahrwesen | 1991


    Sulfidation Corrosion of Nickel-Base Exhaust Valves

    Clark, Gary C. | SAE Technical Papers | 1975


    Hot Corrosion of Diesel Engine Exhaust Valves

    Chaudhuri, Asim | SAE Technical Papers | 1973


    Sulfidation corrosion of nickel- base exhaust valves.

    Clark,G.C. / TRW Inc. | Kraftfahrwesen | 1975


    Corrosion studies of different metal coatings for automotive exhaust applications

    Yasir, Muhammad / Mori, Gregor / Özer, S. Can et al. | Tema Archiv | 2011