Two applications of x-ray residual stress measurements in steel are reported. One application shows how residual stresses have a direct bearing on fatigue strength caused by varying material and heat treatment. The other application shows how x-ray diffraction measurements can help determine the cause of grinder cracking in carburized and hardened steel parts. Grinder cracking occurs by overheating the surface which produces tensile residual stresses that exceed the fracture strength of the steel. Also, there appears to be a relationship between retained austenite content and the grinder cracking phenomenon.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Applications of Residual Stress Measurements


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1972 Automotive Engineering Congress and Exposition ; 1972



    Erscheinungsdatum :

    01.02.1972




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Residual Stress Measurements in Case-Hardened Steels

    Horisawa, Hiroshi / Motoyama, Moritaro | SAE Technical Papers | 1971


    Residual Stress Measurements of Retrofitted Tank Car Weldments

    R. K. Larson / R. L. Florom / B. R. Rajkumar | NTIS | 1992


    Ultrasonic measurements of residual stress in railroad wheels

    Schramm, R.E. / Clark, A.V. / Mitrakovic, D.V. et al. | Tema Archiv | 1991


    Repeatability of Residual Stress Measurements (AIAA 2015-0388)

    Dewald, Adrian / Hill, Michael R. | British Library Conference Proceedings | 2015