An investigation was made of the effect of material, quench severity and case depth on residual stress produced by carburizing. The distribution of stress was affected by carbon gradient and its effect on the Ms temperature in relation to the temperature gradient as influenced by quench severity. The maximum compressive stress was produced outside the case-core boundary near the location of initial transformation. With a more severe quench, it was brought out near the surface, resulting in a higher stress at the surface.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Residual Stress Measurements in Case-Hardened Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1971 Automotive Engineering Congress and Exposition ; 1971



    Erscheinungsdatum :

    01.02.1971




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :




    The Effect of Prior Microstructure on the Hardness and Residual Stress Distribution in Induction Hardened Steels

    Brooks, C. R. / Canale, L. C. F. / Watkins, T. R. et al. | SAE Technical Papers | 2002


    Residual Stress in the Induction Hardened Surface of Steel, 1971

    Ishii, Kentaro / Iwamoto, Mitugi / Shiraiwa, Toshio et al. | SAE Technical Papers | 1971


    Residual Stress in the Induction Hardened Surface of Steel, 1969

    Ishii, Kentaro / Iwamoto, Mitugi / Shiraiwa, Toshio et al. | SAE Technical Papers | 1969