This paper is concerned with press forming of work hardened or age hardened aluminum alloy sheet at temperatures in the range 100-300°C. By controlling the time and temperature of forming below that necessary for recrystallization or over-aging the formability is significantly enhanced while a high room temperature tensile strength is maintained. It is shown by both laboratory measurements and plant trials that it is possible to warm form high strength aluminum sheet into complex parts. A brief discussion is given on some of the important materials and process considerations.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Warm Forming High-Strength Aluminum Automotive Parts


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1977 International Automotive Engineering Congress and Exposition ; 1977



    Erscheinungsdatum :

    01.02.1977




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Application of warm forming aluminum alloy parts for automotive body based on impact

    Sun, H. T. / Wang, J. / Shen, G. Z. et al. | Springer Verlag | 2013


    Application of warm forming aluminum alloy parts for automotive body based on impact

    Sun, H. T. / Wang, J. / Shen, G. Z. et al. | Online Contents | 2013


    Application of warm forming aluminum alloy parts for automotive body based on impact

    Sun, H. T. / Wang, J. / Shen, G. Z. et al. | British Library Online Contents | 2013



    High-strength aluminum automotive alloy

    Childree, D. | Tema Archiv | 1998