HAYNES® NS-163® alloy was developed by Haynes International Inc., Kokomo, IN, for high-temperature structural applications by pursuing a dual manufacturing approach: the fabrication of components in the readily weldable and formable mill-annealed condition, and their subsequent strengthening by means of a gas nitriding process. The latter process results in dispersion-strengthening by virtue of formation of internal nitrides. Since this process is diffusion-controlled, component section thicknesses are limited to approximately 2.0 mm (0.080 in.). Microstructures and mechanical properties of nitrided sheet samples are presented. Oxidation resistance and the need for coatings at temperatures exceeding 980 °C (1800 °F) are addressed as well.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    HAYNES NS-163 Alloy: A Novel Nitride Dispersion-Strengthened CO-Base Alloy




    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    52.52 Thermische Energieerzeugung, Wärmetechnik / 52.30 Strömungskraftmaschinen, Turbomaschinen / 52.52 / 52.30



    Oxide dispersion strengthened refractory base alloy

    DI DOMIZIO ROBERT / DETOR ANDREW JOSEPH / RUUD JAMES ANTHONY et al. | Europäisches Patentamt | 2022

    Freier Zugriff

    Considerations About the Aluminium Dispersion Strengthened Alloy

    Sfat, Catalin / Vasilescu, Marius / Vasile, Toma | SAE Technical Papers | 2002


    Considerations about the Aluminium Dispersion Strengthened Alloy

    Vasilescu, M. / Sfat, C. / Vasile, T. et al. | British Library Conference Proceedings | 2002


    Considerations about the Aluminium Dispersion Strengthened Alloy

    Sfat, Catalin / Vasilescu, Marius / Vasile, Toma | SAE Technical Papers | 2002


    Considerations about the aluminium dispersion strengthened alloy

    Vasilescu,M. / Sfat,C. / Vasile,T. et al. | Kraftfahrwesen | 2002