New fabrication method produces pinhole-free film of cobalt silicide on silicon substrate. In new method, cobalt and silicon evaporated from electron-beam sources onto substrate of silicon having <111> crystal orientation. Materials deposited in stoichiometric ratio of two silicon atoms to one of cobalt, yielding single-crystal CoSi2 film 5 to 10 nm thick. Layer of amorphous silicon 1 to 2 nm thick deposited on CoSi2. Specimen then annealed at 550 degree C for 10 min. Absence of pinholes critical to operation of multilayer devices employing CoSi2 layers, such as metal base transistor.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Deposition Of Pinhole-Free CoSi2 Film


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    01.06.1989



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Making Submicron CoSi2 Structures On Silicon Substrates

    Nieh, Simon K. W. / Lin, True-Lon / Fathauer, Robert W. | NTRS | 1989


    Pinhole inspection device

    BAE SEONGHO | Europäisches Patentamt | 2025

    Freier Zugriff

    Pinhole diffraction filter

    Woodgate, B. E. | NTRS | 1977



    Combustion Pinhole-Camera System

    A. B. Witte | NTIS | 1982