Early detection of fatigue damage in composite materials by nondestructive inspection (NDI) techniques has been demonstrated for glass/epoxy, graphite/glass/epoxy, and graphite/epoxy composites. Modulus and temperature were monitored and a correlation between them observed. Axial modulus and torsional modulus changes were a function of the laminate orientation. Torsional modulus measurements and coin tap tests were performed at 0, 1 million, 5 million, and 10 million cycles, on axial fatigue specimens. Three distinct regions were noted. In the primary region a small but rapid change in stiffness was noted in the first few thousand cycles. This was followed by a secondary region of little or no stiffness change. The tertiary region was characterized by an increasing rate of stiffness change leading to fracture. NDI procedures including holographic interferometry, ultrasonics, penetrant, and X-ray radiography were evaluated for fatigue damage detection.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Early detection of fatigue damage in composite materials


    Beteiligte:
    Salkind, M. J. (Autor:in)

    Kongress:

    AIAA, ASME, and SAE, Structures, Structural Dynamics, and Materials Conference ; 1975 ; Denver, CO


    Erscheinungsdatum :

    1975-05-01


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :





    Characterization of fatigue damage in composite sandwich hull materials at low temperatures

    Soni, Samirkumar M. / Gibson, Ronald F. / Ayorinde, Emmanuel O. | Tema Archiv | 2007


    Fatigue Damage Mechanisms and their Evolution in Composite Materials for Aeronautical Applications

    Salvetti, A. / Lazzeri, L. / Giavotto, V. et al. | British Library Conference Proceedings | 1989