This paper summarizes the results of experimental and numerical studies on the fatigue behavior of foam core carbon/epoxy composite sandwich (CS) beams at room temperature (RT) and low temperatures (down to -60 Degree Celsius) for their potential applicability in the hull materials of ships navigating in the Polar Regions. 4-point static flexural test results confirmed the clear effects of low temperatures on the stiffness, strength, elastic limit and brittleness of the CS beams. Core shear was found to be the dominant failure mode under fatigue loading conditions at -60 Degree Celsius. Significant increases in the useful fatigue life with brittle type core shear failure were observed at low temperatures by comparison with the corresponding RT behavior. Two approaches were used to investigate stiffness reductions during useful fatigue life. The static finite element analysis (FEA) explained the effects of skin stiffness on the crack initiation location under fatigue loading conditions.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Characterization of fatigue damage in composite sandwich hull materials at low temperatures


    Beteiligte:


    Erscheinungsdatum :

    2007


    Format / Umfang :

    10 Seiten, 11 Bilder, 1 Tabelle, 16 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch




    Hull Structure Fatigue Life with Consideration of Fatigue Damage Initiation and Development

    Boitsov, G. V. / Knoring, S. D. / Paliy, O. M. et al. | British Library Conference Proceedings | 2003


    Onboard monitoring of fatigue damage rates in the hull girder

    Nielsen, U. D. / Jensen, J. J. / Pedersen, P. T. et al. | British Library Online Contents | 2011


    A FOAM SANDWICH SUBMARINE HULL DERA `NOVEL HULL MODEL NO. 1'

    Smith, J. R. / Graham, D. / Creswell, D. J. et al. | British Library Conference Proceedings | 1999


    Method for producing a hull wall from a fiber composite sandwich component

    DIERKES DOMINIK | Europäisches Patentamt | 2021

    Freier Zugriff

    Damage Assessment for Composite Sandwich Structure

    Walker, Thomas / Graesser, Douglas / Ward, Stephen et al. | AIAA | 2003