A survey of aircraft wheel failures, and a review of the parameters involved in the qualification tests for aircraft wheels, indicated a need for accurate information concerning wheel service loading conditions in order to formulate realistic wheel fatigue test spectra. The fractographic examination of three types of wheels from modern aircraft has emphasized the significance of corrosion in the nucleation of fatigue cracks, and has indicated that landing impact loads and brake applications at high speeds may contribute to the growth of the cracks. Several types of macroscopic growth 'bands' or 'lines' that are frequently observed on the fatigue fracture surfaces of laboratory specimens and of components that have failed in service, have been cited and described. Those lines observed on the fracture surfaces of the failed wheels were correlated with crack growth during aircraft landing cycles. The derivation of fatigue crack growth rate information from these lines has facilitated the revision of wheel inspection schedules with the purpose of preventing the catastrophic failure of aircraft wheels. (Author)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    A Fractographic Study of the Fatigue Failure of Aircraft Wheels


    Beteiligte:
    W. Wiebe (Autor:in)

    Erscheinungsdatum :

    1970


    Format / Umfang :

    31 pages


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch





    Fractographic study of fatigue cracks in a steel car wheel

    Zheng, Zhanguang / Yuan, Shuai / Sun, Teng et al. | Tema Archiv | 2015


    FEA Cyclic Symmetric Fatigue Analysis of Aircraft Wheels

    Fish, Bradley E. / Patterson, Delbert K. / Pajot, Joseph J. | SAE Technical Papers | 2002


    FEA Cyclic Symmetric Fatigue Analysis of Aircraft Wheels

    Fish, B. E. / Pajot, J. J. / Patterson, D. K. et al. | British Library Conference Proceedings | 2002