Spanentstehungsprozeß an einer polierten, angeätzten Probe beim Orthogonalschnitt. Die Spanbildung wechselt wegen unterschiedlicher Orientierungen der groben Kristallite. Diese Orientierungsabhängigkeit der Spanungskenngrößen überdeckt den Einfluß der Spanungsdicke auf die Spanbildung.

    The film shows how chippings are produced from a polished and etched testing workpiece made of the aluminium forging alloy AlCuMgPb, during orthogonal cutting. Because of the coarse-cristalline structure, with grains considerably larger than the maximum chip thickness, cutting causes the formation of chippings of varying appearance in individual crystals of differing orientation. The shearing area, chip-producing mechanism and visible deformation of the workpiece change with the different types of chip, from flowing chip to shearing chip. The influence on the chipping thickness is concealed by the fact that the chip-production is a direct result of the structure orientation in this coarse, polycrystalline material.


    Zugriff

    Zum TIB AV-Portal


    Exportieren, teilen und zitieren



    Titel :

    Zerspanen der Aluminium-Legierung AlCuMgPb: Schnittvorgang im Feingefüge Variation der Spanungsdicke


    Untertitel :

    Documentation/Report


    Weitere Titelangaben:

    Machining of the AlCuMgPb Aluminum Alloy - Cutting Process in the Microstructure; Thickness Variation of the Chip


    Beteiligte:

    Erscheinungsdatum :

    01.01.1971


    Format / Umfang :

    68MB, 00:05:33:00


    Anmerkungen:

    Stummfilm
    Silent movie



    Medientyp :

    Audiovisuelles Material


    Format :

    Audiovisuelles Material


    Sprache :

    Unbekannt





    Vorschau

    Preview Image