Spanentstehungsprozeß an einer polierten, angeätzten Probe beim Orthogonalschnitt. Schrittweise Erhöhung der Schnittgeschwindigkeit (0,01 - 5 m/min) beeinflußt vor allem die Aufbauschneidenbildung. Bei hohen Schnittgeschwindigkeiten übernimmt die Aufbauschneide die Funktion des Schneidkeils. Mit Zeitdehnung.

    The film shows how chippings are produced from a polished and etched testing workpiece made of casehardening steel 16MnCr 5 during orthogonal cutting. The individual areas and stages of deformation during the formation of flowing chips are particularly worth watching in this markedly ferrito-perlitic structure. The effect of the cutting speed (0.01 to 5 m/min.) is shown firstly in the formation of pick-up on the cutting edge, which assumes unusual shapes particularly with large items, so that the formation of chips is also affected by the changed geometry of the cutting edges.


    Zugriff

    Zum TIB AV-Portal


    Exportieren, teilen und zitieren



    Titel :

    Zerspanen von Stahl 16 MnCr 5: Schnittvorgang im Feingefüge Variation der Schnittgeschwindigkeit


    Untertitel :

    Documentation/Report


    Weitere Titelangaben:

    Machining of 16 MnCr 5 Steel - Cutting Process in the Microstructure; Variation of the Cutting Speed


    Beteiligte:

    Erscheinungsdatum :

    01.01.1970


    Format / Umfang :

    75MB, 00:06:07:00


    Anmerkungen:

    Stummfilm
    Silent movie



    Medientyp :

    Audiovisuelles Material


    Format :

    Audiovisuelles Material


    Sprache :

    Unbekannt





    Vorschau

    Preview Image