Mit zunehmender Spanungsdicke wird die Fließspanbildung und damit auch die Struktur im Span gleichförmiger. Die Werkstoffbeanspruchung ändert sich mit der Spanungsdicke, erkennbar an der Ausbildung der Aufbauschneide. Geringe Zeitdehnung.
The film shows the process of chip formation on a polished and etched specimen of C 45 W 3 unalloyed tool steel. The various phenomena of chip formation and the individual deformation processes can be observed particularly well in the perlitic-ferritic structure of the material. As the chip thickness increases from 4 to 55 µm the formation of flow chips, that is to say the shearing strain and, associated with it, the texture of the chips, become more uniform. The stresses and strains to which the material is subjected in the chip formation zone vary with chip thickness which also manifests itself in the build-up of material on the cutting edge.
Zerspanen von Stahl C 45 W 3: Schnittvorgang im Feingefüge Variation der Spanungsdicke
Documentation/Report
Machining of C 45 W 3 Steel - Cutting Process in the Microstructure; Thickness Variation of the Chip
1975-01-01
217MB, 00:03:42:00
Stummfilm
Silent movie
Audiovisuelles Material
Audiovisuelles Material
Unbekannt
Stahl / Zerspanung , Zerspanung / Stahl , Aufbauschneidenbildung , Spanbildung / Fließspanbildung / Metall , Fertigungstechnik , spanende Bearbeitung , Stahl , Technik steel / machining , machining / steel , chip formation / metal , built-up edge formation , Encyclopaedia Cinematographica , production engineering , steel , swarf machining , technology
Zerspanen metallischer Werkstoffe - Spanentstehung: Schnittvorgang im Feingefüge
TIB AV-Portal | 1977
|Zerspanen von Stahl C 45 W 3: Schnittvorgang im Feingefüge Variation des Schneidenradius
TIB AV-Portal | 1975
|Zerspanen von Stahl C 45 W 3: Schnittvorgang im Feingefüge Variation des Spanwinkels
TIB AV-Portal | 1975
|