Beim Orthogonalschnitt entsteht an dem weichgeglühten und feinkörnigen perlitischen Gefüge ein relativ gleichmäßiger Fließspan bei gut sichtbarer Stauch- und Keilwirkung im Verformungsbereich. Zeitdehnung.
The film shows the process of chip formation in the orthogonal cutting of a polished and etched specimen of 100 Cr 6 steel used in the manufacture of anti-friction bearings. A relatively uniform flow chip forms in the softannealed and fine-grained perlitic structure, with the upsetting and wedging action caused by the wedge-like part of the cutting tool being readily discernible in the region of deformation. The build-up of material on the cutting edge is particularly noticeable at a cutting speed of 20 metres per minute.
Zerspanen von Stahl 100 Cr 6: Schnittvorgang im Feingefüge
Documentation/Report
Machining of 100 Cr 6 Steel - Cutting Process in the Microstructure
01.01.1975
60MB, 00:04:56:00
Stummfilm
Silent movie
Audiovisuelles Material
Audiovisuelles Material
Unbekannt
Fertigungstechnik , Zerspanung / Stahl , spanende Bearbeitung , Aufbauschneidenbildung , Spanbildung / Fließspanbildung / Metall , Stahl , Stahl / Zerspanung , Technik Encyclopaedia Cinematographica , machining / steel , technology , steel , steel / machining , production engineering , chip formation / metal , swarf machining , built-up edge formation
Zerspanen metallischer Werkstoffe - Spanentstehung: Schnittvorgang im Feingefüge
TIB AV-Portal | 1977
|Zerspanen von Stahl C 45 W 3: Schnittvorgang im Feingefüge Variation des Schneidenradius
TIB AV-Portal | 1975
|Zerspanen von Stahl C 45 W 3: Schnittvorgang im Feingefüge Variation des Spanwinkels
TIB AV-Portal | 1975
|