The invention relates to a method for preparing a positive electrode material for a lithium ion battery. The method comprises the following steps: 1) dispersing graphene oxide, a carbon nanotube, a nitrogen doping agent, a raw material selected from a lithium iron phosphate material and a lithium iron phosphate precursor, and an optional ternary material in water to obtain a mixture A; 2) freeze-drying the mixture A obtained in the step 1) to obtain three-dimensional graphene oxide loaded with the raw material and an optional ternary material; and 3) placing the three-dimensional graphene oxide obtained in the step 2) in an inert gas atmosphere at a sintering temperature in a range of 500-800 DEG C for 5-30 hours to obtain the positive electrode material. The battery comprising the positive electrode material prepared by the method provided by the invention has improved rate capability and cycling stability.

    本发明涉及一种制备用于锂离子电池的正极材料的方法。所述方法包括如下步骤:1)将氧化石墨烯、碳纳米管、氮掺杂剂、选自磷酸铁锂材料和磷酸铁锂前驱体的原料、任选的三元材料在水中分散后得到混合物A;2)将步骤1)所得的混合物A冷冻干燥得到负载有所述原料和任选的三元材料的三维氧化石墨烯;和3)将步骤2)所得的三维氧化石墨烯置于惰性气体氛围下和500‑800℃范围内的烧结温度下保持5‑30小时,得到所述正极材料。包含由本发明的方法制备的正极材料的电池具有提高的倍率性能和循环稳定性。


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Method for preparing positive electrode material for lithium ion battery


    Weitere Titelangaben:

    制备用于锂离子电池的正极材料的方法


    Beteiligte:
    ZENG SHIZHE (Autor:in)

    Erscheinungsdatum :

    10.10.2023


    Medientyp :

    Patent


    Format :

    Elektronische Ressource


    Sprache :

    Chinesisch


    Klassifikation :

    IPC:    H01M Verfahren oder Mittel, z.B. Batterien, für die direkte Umwandlung von chemischer in elektrische Energie , PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY / B60L PROPULSION OF ELECTRICALLY-PROPELLED VEHICLES , Antrieb von elektrisch angetriebenen Fahrzeugen



    POSITIVE ELECTRODE MATERIAL FOR LITHIUM SECONDARY BATTERY

    SAWAI TAKEHIKO / SAITO SHINJI / URAO KAZUNORI et al. | Europäisches Patentamt | 2016

    Freier Zugriff

    POSITIVE ELECTRODE MATERIAL FOR LITHIUM SECONDARY BATTERY

    SAWAI TAKEHIKO / SAITO SHINJI / URAO KAZUNORI et al. | Europäisches Patentamt | 2018

    Freier Zugriff

    Positive electrode material for lithium secondary battery

    SAWAI TAKEHIKO / SAITO SHINJI / URAO KAZUNORI et al. | Europäisches Patentamt | 2019

    Freier Zugriff

    POSITIVE ELECTRODE MATERIAL FOR LITHIUM SECONDARY BATTERY

    SAWAI TAKEHIKO / SAITO SHINJI / URAO KAZUNORI et al. | Europäisches Patentamt | 2022

    Freier Zugriff

    2 POSITIVE ELECTRODE MATERIAL FOR LITHIUM SECONDARY BATTERY

    Europäisches Patentamt | 2021

    Freier Zugriff