The invention provides a tread rubber composition with low hysteresis loss, a mixing method and a car tire, and belongs to the field of rubber tire manufacturing. The tread rubber composition with low hysteresis loss is prepared from the following components in parts by mass: 100 parts of matrix rubber, 40-80 parts of a reinforcing filling material, 1.6-6.4 parts of a silane coupling agent, 1-4 parts of a white carbon black dispersing agent, 0-10 parts of environment-friendly rubber operating oil, 3-5 parts of an active agent, 3-7 parts of an anti-aging agent, 1-4 parts of a vulcanizing agent and 2-4 parts of an accelerant, the matrix rubber is a diene elastomer and comprises 60-100 parts of a first diene elastomer, 0-30 parts of a second diene elastomer and 0-20 parts of a third diene elastomer; the content of the diene elastomer in the tread rubber composition is more than 50%; the Shore hardness of the tread rubber composition is 64-68 degrees, the tensile strength of the tread rubber composition is larger than or equal to 16 MPa, and the hysteresis loss tan delta at 70 DEG C of the tread rubber composition is smaller than 0.050. The tread rubber composition disclosed by the invention has ultralow hysteresis loss, excellent material mechanical property and good processing property.

    本发明提出一种低滞后损失的胎面橡胶组合物、混炼方法及轿车轮胎,属于橡胶轮胎制造领域。该低滞后损失的胎面橡胶组合物,按照质量份计,包括下列组分:基体橡胶100份,补强填充材料40‑80份,硅烷偶联剂1.6‑6.4份,白炭黑分散剂1‑4份,环保橡胶操作油0‑10份,活性剂3‑5份,防老剂3‑7份,硫化剂1‑4份,促进剂2‑4份;基体橡胶为二烯类弹性体,包括第一二烯类弹性体60‑100份,第二二烯类弹性体0‑30份,第三二烯类弹性体0‑20份;胎面橡胶组合物中的二烯类弹性体含量在50%以上;胎面橡胶组合物的邵氏硬度为64‑68度,胎面橡胶组合物的拉伸强度≥16MPa,胎面橡胶组合物的滞后损失tanδ@70℃<0.050。本发明胎面橡胶组合物具有超低的滞后损失、优异的材料力学性能、良好的加工工艺性能。


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Tread rubber composition with low hysteresis loss, mixing method and car tire


    Weitere Titelangaben:

    一种低滞后损失的胎面橡胶组合物、混炼方法及轿车轮胎


    Beteiligte:
    HUANG YIGANG (Autor:in) / WANG QIAOPING (Autor:in) / WANG JUN (Autor:in) / SUN SHUMEI (Autor:in) / WANG ZIQI (Autor:in) / SU MING (Autor:in) / HAN DAN (Autor:in) / ZHANG JING (Autor:in) / SUN ZHENG (Autor:in) / XU BING (Autor:in)

    Erscheinungsdatum :

    2023-05-23


    Medientyp :

    Patent


    Format :

    Elektronische Ressource


    Sprache :

    Chinesisch


    Klassifikation :

    IPC:    C08L COMPOSITIONS OF MACROMOLECULAR COMPOUNDS , Massen auf Basis makromolekularer Verbindungen / B60C VEHICLE TYRES , Fahrzeugreifen / C08K Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe , USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS



    RUBBER COMPOSITION FOR TIRE TREAD, TIRE TREAD, AND TIRE

    HORIUCHI NATSUKI | Europäisches Patentamt | 2019

    Freier Zugriff

    Tire tread rubber composition

    WANG FENG / WANG JUNYING / SUN TAO et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Tire tread rubber composition

    ZAMA AYA | Europäisches Patentamt | 2022

    Freier Zugriff

    Tire Tread Rubber Composition

    KLECKNER JAMES P / UNGER ANTHONY M / GALIZIO BENJAMIN C | Europäisches Patentamt | 2021

    Freier Zugriff

    Tire Tread Rubber Composition

    UNGER ANTHONY M / STALNAKER ADRIAN C / PLACKE JESSICA L et al. | Europäisches Patentamt | 2021

    Freier Zugriff