New casting method by permanent mold made of carbon and silicon carbide was developed to refine casting process of rolling stock pieces of cast iron; rectangular molds were used in preliminary experiments and molds of brake block were made and tested; as result of repeated experiments, permanent mold containing SiC 40 to 60%, compressive strength being 300 to 350 kg/sq cm, is recommended as optimum.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    C-SIC permanent mold casting of brake block


    Weitere Titelangaben:

    Tokyo. Ry Tech Research Inst -- Quarterly Report


    Beteiligte:
    Shimada, H. (Autor:in) / Yoshikawa, T. (Autor:in)


    Erscheinungsdatum :

    1967


    Format / Umfang :

    5 pages


    Medientyp :

    Report


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    Permanent Mold Gravity Casting Cylinder Block with Hypereutectic Aluminum Liners

    Fuganti, A. / Mus, C. / Salinas, D. et al. | SAE Technical Papers | 2001


    Permanent mold gravity casting cylinder block with hypereutectic aluminum liners

    Crivellone,G. / Fuganti,A. / Mus,C. et al. | Kraftfahrwesen | 2001


    2001-01-0402 Permanent Mold Gravity Casting Cylinder Block with Hypereutectic Aluminum Liners

    Crivellone, G. / Fuganti, A. / Mus, C. et al. | British Library Conference Proceedings | 2001


    Permanent mold casting of aluminum at Fiat

    Gallo, S. | Tema Archiv | 1979


    New approaches in microcasting: permanent mold casting and composite casting

    Baumeister, G. / Buqezi-Ahmeti, D. / Glaser, J. et al. | British Library Online Contents | 2011