A resin-transfer-molding (RTM) polyimide resin, RTM-PI, was developed, and the matrix-graded polyimide composite along thickness directions was fabricated with RTM processing. The matrix-graded composite was composed of surface layers with polyimide matrix having high thermal stability, and core layers with RTM-PI matrix. The RTM processing parameters were established based on thermogravimetry, rheology and curing data of PI resins. The results show that RTM-PI resin exhibits the properties of low viscosity, super long processable time, and high thermal resistance. The lowest viscosity is below 0.1 Pa·s, processable time is longer than 300 min, and glass-transition-temperature reaches 445 ℃. The internal quality of the matrix-graded polyimide composite along thickness direction is excellent, and the reduction of mass loss after the thermal ageing at 350 ℃ for 100 h is more than 48% lower than that of the pure RTM-PI composite.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Preparation and characterization of matrix-graded polyimide composite along thickness direction


    Beteiligte:
    NI Hongjiang (Autor:in) / LI Jun (Autor:in) / XING Yu (Autor:in) / ZHANG Daijun (Autor:in) / CHEN Xiangbao (Autor:in)


    Erscheinungsdatum :

    2022




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Characterization of Polyimide Composite Ribbon Weld Bonding

    Hinkley, J. A. / Marchello, J. M. / Messier, B. C. et al. | British Library Conference Proceedings | 1996


    Novel polyimide composite film material with high along-surface electric strength and preparation method and application thereof

    ZHANG GUANJUN / LI WENRUI / YANG XIONG et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Vapor-deposited graded-thickness films

    Herzig, H. / Spencer, R. S. | NTRS | 1979


    Polyimide fibrofelt prepreg, preparation method thereof, composite material and application

    LIU SHAOFEI / ZHAN JIAYU / WANG ZIQI et al. | Europäisches Patentamt | 2024

    Freier Zugriff

    Fiber Study Involving a Polyimide Matrix

    Cano, R. J. / Rommel, M. / Hinkley, J. A. et al. | British Library Conference Proceedings | 1996